Transactions of Nonferrous Metals Society of China (中国有色金属学报)•2026•DOI: 10.1016/S1003-6326(26)67065-3

Single Crystal NCM811 Cathode Material Prepared by Rapid Solvothermal Method

Polycrystalline LiNi0.8Co0.1Mn0.1O2 (NCM811) cathodes undergo intergranular cracking and structural collapse during extended cycling, limiting their commercial viability. This study reports single-crystalline NCM811 synthesized via a rapid ethanol–water solvothermal method. The solvothermal duration was varied, and the 60 min sample (NCM-60) exhibited optimal electrochemical performance. X-ray diffractometry confirmed an α-NaFeO2 structure with R-3m space group and high crystallinity. NCM-60 delivered a reversible capacity of 157.28 mA·h/g at 1C and a capacity retention of 55.06% after 200 cycles, significantly outperforming polycrystalline NCM (PC-NCM). Cross-sectional scanning electron microscopy revealed no apparent cracks in NCM-60 after 200 cycles, whereas PC-NCM exhibited severe intergranular fracture. The results demonstrate that shortening solvothermal time reduces precursor particle size and crystallinity, but 60 min yields the best balance. Pre-oxidation of the carbonate precursor before lithiation is recommended to mitigate CO2 evolution and lithium–nickel disorder during high-temperature sintering. This rapid solvothermal route offers a scalable pathway to single-crystal NCM811 with enhanced cycling stability and mechanical integrity.

Read Full Analysis→Download Authentic PDF

Journal of Central South University•2026•DOI: 10.1007/s11771-026-6187-4

An acid-free process for the selective recovery of lithium from spent ternary lithium-ion batteries

With the dramatic accumulation of the end-of-life lithium-ion batteries, their recycling is attracting extensive attention worldwide. To address the problem of low lithium recovery in the current typical hydrometallurgy recovery process, this research uses sodium bisulfate as an auxiliary roasting reagent to extract lithium from spent lithium-ion batteries through sulphation roasting, which can enhance the lithium recovery rate significantly. A systematic study of the sulphation roasting process and the mechanisms was carried out with experiments, thermodynamic calculations, and characterization of the roasted sample phases. The results showed that at a roasting temperature of 600 °C, NaHSO4·H2O/spent LiNixCoyMnzO2 cathode powders (S-NCM) mass ratio of 1.2, and roasting time of 60 min, 95% selective dissolution of lithium was acquired, while the leaching rates of Ni, Co, and Mn were confined under 1%. During roasting, the NCM layered structure collapses and the lithium is transformed into the LiNaSO4 phase, while the transition metals transform into Ni6MnO8 and MnCo2O4 phases. The removal of impurity ions from the lithium-rich leaching solution and the generation of Li2CO3 were achieved by a combination of thermodynamic calculations and experiments.

Read Full Analysis→Download Authentic PDF

Int. Journal of Minerals, Metallurgy and Materials (矿物冶金与材料学报)•2025•DOI: 10.1007/s12613-024-3004-7

High efficiency reduction leaching of iron phosphate residue from the recycling of spent LiFePO4 battery

The effective reuse of iron phosphate residue (IPR) is the key issue in the recycling of spent LiFePO4 batteries. Therefore, in this study, the reduction leaching of IPR in H2SO4 solution by adding iron powder as reducing agent was investigated and compared with direct leaching. The results show that the leaching rate of IPR reached 97% under the optimum reduction leaching conditions. Kinetic studies show that the activation energy for reduction leaching is 12.71 kJ/mol, while that of direct leaching is 21.57 kJ/mol. Moreover, the reduction leaching time is reduced by half and the acid consumption is reduced by 30% compared to direct leaching with the same leaching rate. This work provides a scientific guidance to the treatment of iron phosphate residue from the recycling of spent LiFePO4 batteries.

Read Full Analysis→Download Authentic PDF